Mold transient heat transfer behavior based on measurement

and inverse analysis of slab continuous casting

رفتار انتقال حرارت ناپایدار قالب بر اساس اندازه‎گیری و آنالیز معکوس ورق

تهیه شده به روش ریخته‎گری مداوم

ABSTRACT

The experiment is conducted on an arc slab caster, liquid steel flows into mold from tundish by submerged entry nozzle with target meniscus height of 82 mm, and slag is manually added. In two horizontal cross sections with distances of 190 and 390 mm respectively from the mold top, sum up 24 pairs of thermocouples are embedded into the mold, 10 for each wide face (outside radius face and inside radius face) and 2 for each narrow face (left narrow face and right narrow face). Fig. 1 details the layout of the thermocouples in the mold. The row of thermocouples is labeled “R,” whereas the column is labeled “C.” For instance, R1C3 is the cross point of the first row and the third column. The detecting frequency of mold temperature is 1 Hz.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

آزمایش روی یک چرخک ورقی قوسی هدایت می‎شود، فولاد مایع از تاندیش توسط نازل ورودی پوشانده شده با ارتفاع ناحیه‎ی هلالی مورد نظر ۸۲ mm تبه سمت قالب جریان می‎یابد و سرباره به صورت دستی به آن اضافه می‎شود. در دو مقطع عرضی افقی با فواصل به ترتیب mm190 و mm390 از بالای قالب، در مجموع ۲۴ جفت ترموکوپل در قالب جاسازی می‎شود، برای هر وجه بزرگ ده عدد (وجه شعاع خارجی و وجه شعاع داخلی) و دو عدد برای هر وجه باریک (وجه باریک سمت چپی و وجه باریک سمت راستی). شکل۱ چیدمان ترموکوپل‎ها را در قالب نشان می‎دهد. ردیف ترموکوپل‎ها با علامت R در حالیکه ستون آن با علامت C نامگذاری می‎شود. برای مثال R1C3  نقطه‎ی تقاطع اولین ردیف و سومین ستون است. فرکانس تعیین شده‎ی دمای قالب برابر با ۱ Hz است.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.