Fine structure at the diffusion welded interface of Fe3Al/Q235 dissimilar materials
ساختار ریز (ظریف) فصل مشترک جوش نفوذی اتصال Fe3Al/Q235 غیر هم جنس
ABSTRACT
In recent years, considerable interest has been generated in intermetallic compounds because intermetallic compounds have unique properties, such as high yield strength at high temperature and excellent oxidation and corrosion resistance because of their long range ordered structure and coexistence of metallic bond (Mckameey et al 1991). When specially compared to other intermetallic compounds such as Ni3Al and Ti3Al, Fe3Al is cheaper and its strength increases with the increase of temperature below 600°C (Rabin et al 1994). Fe3Al is thought of as one of the most prospective structural materials in industry. At the same time, the weldability also has attracted the attention of several researchers (David et al 1989; Gao et al 2000).
جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید.
چکیده
در این مقاله، اتصال Fe3Al/Q235 به طور موفقیت آمیز به روش پیشرفته جوش نفوذی در خلأ ایجاد شد. مشخصه های ریز ساختاری در محل فصل مشترک به کمک میکروسکوپ الکترونی روبشی (SEM) مورد بررسی قرار گرفت. از پراش پرتو ایکس (XRD) به منظور بررسی ساختار فازی استفاده شد. ترکیب شیمیایی در محل فصل مشترک Fe3Al/Q235 و جهت گیری شبکه بین فازهای Fe3Al و FeAl و محلول جامد α-Fe(Al) با استفاده از میکروسک الکترونی عبوری (TEM) مطالعه شدند. این مقاله برای بررسی جوش پذیری Fe3Al و افزایش کاربرد این ترکیب بین فلزی بسیار حائز اهمیت می باشد. فصل مشترک اتصال غیر همجنس Fe3Al/Q235 که به روش جوش نفوذی در خلأ آماده شده، دارای پیوستگی عالی می باشد.
جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.
دیدگاه‌ها (0)
نقد و بررسی‌ها
هیچ دیدگاهی برای این محصول نوشته نشده است.
.فقط مشتریانی که این محصول را خریداری کرده اند و وارد سیستم شده اند میتوانند برای این محصول دیدگاه(نظر) ارسال کنند.