Gas content in high pressure die castings

درصد گاز در ریخته­ گری دایکاست فشار بالا

ABSTRACT

This paper presents the results of a quantitative study of the gas level in various types of castings from the high pressure die casting (HPDC) process using a vacuum fusion method. It was found that the major part of the gas was from the air entrapment during cavity filling. Other sources such as air entrapment during ladling, residual die lubricant and quenching water were also noticeable. Measurements of a large casting and castings from a multi-cavity die showed that the gas content was unevenly distributed. The modified vacuum fusion method has been proved to be a valuable tool for evaluating and quantifying the level of gas in castings as well as for an assessment of the influence of different process parameters on gas evolution in castings.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

این مقاله نتایج مطالعات کمی درصد گاز در انواع مختلف از ریخته­ گری دایکاست فشار بالا HPDC با استفاده از روش ذوب تحت خلا نشان می­ دهد. بخش اصلی گاز از حبس هوا درطی پرکردن قالب صورت می ­گیرد. منابع دیگر مثل حبس هوا درطی ملاقه­ کشی است و روانساز پسماند در قالب و آب کوئنچ را باید درنظر گرفت. اندازه­ گیری­ های ریخته گری بزرگ و چند قالبه درصد گاز بطور غیریکنواخت وجود خواهد داشت. روش ذوب تحت خلا برای ابزار ارزیابی و کمی­ سازی درصد گاز در ریخته­ گری استفاده شده و اثر پارامترهای مختلف برروی تکامل گاز در ریخته­ گری می­ باشد .

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.