ریزساختارها و انحراف جهت گیری رشد دندریت فاز Al2Cu

Characterization of microstructures and growth orientation deviating

of Al2Cu phase dendrite at different directional solidification rates

مشخصه یابی ریزساختارها و انحراف جهت گیری رشد دندریت فاز Al2Cu

در نرخ های انجماد جهت دار مختلف

ABSTRACT

At different directional solidification rates (10, 20 and 100 mm/s), microstructures and growth orientation variations of Al2Cu dendrite in Al-40%Cu alloy were characterized. When solidification rates were ranged from 10 to 100 mm/s, three-dimensional microstructure of Al2Cu dendrite changed from faceted L-shaped patterns to non-faceted complex dendrite morphology in transverse section. By the macro and micro orientation analysis characterize methods, [001] growth direction of Al2Cu dendrites with different morphologies was determined. The deviation angle between [001] direction and the heat flow direction was increased with solidified rate increasing. The experimental results showed that the regular solidified microstructure and growth orientation along the heat flow direction could be well controlled under lower directional solidification rate.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

در نرخ های انجماد جهت دار مختلف ( 10 ، 20 و μm/s 100 )، ریزساختار و تغییرات جهت گیری رشد دندریت Al2Cu در آلیاژ Al-40% Cu مشخصه یابی شد. هنگامی که نرخ های انجماد در محدوده 10 تا μm/s 100 بود، ریزساختار سه بعدی دندریت Al2Cu از حالت مسطح L-شکل به حالت دندریت پیچیده غیر مسطح در مقطع عرضی تغییر یافت. بوسیله روش های مشخصه یابی آنالیز جهت گیری ماکرو و میکرو، جهت رشد [001] از دندریت های Al2Cu با مورفولوژی های مختلف تعیین شد. زاویه انحراف بین جهت [001] و جهت انتقال حرارت با افزایش نرخ انجماد افزایش یافت. نتایج آزمایشگاهی نشان داد که ریزساختار انجماد یافته و جهت گیری رشد در راستای جهت انتقال حرارت را می توان بخوبی در شرایط نرخ انجماد جهت دار پایین تر کنترل نمود.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.