Achievingultrafine-grained ferrite structure in friction stir processed weld metal

دستیابی به ساختار فریتی فوق ریزدانه در فلز جوش تحت فرایند اصطکاکی اغتشاشی

ABSTRACT

Ultrafine-grained (UFG) ferrite phase was the desired structure in the weld metal of high strength low alloy (HSLA) steel joints. In this study, submerged arc weld metal of a HSLA steel was subjected to friction stir processing (FSP) under a very low rotation rate of 80 rpm. The original coarse bainite structure was changed into UFG ferrite structure after FSP, and the grain sizes were re fined to about 500 and 300 nm in the upper and lower parts of the processed zone, respectively. This study provides an effective strategy to preparing UFG ferrite structure in the weld metal of HSLA steel joints, and also a potential welding method.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

 

دستیابی به فریت فوق ریزدانه تحت فرایند اصطکاکی اغتشاشی

چکیده

فاز فریت فوق ریزدانه ، ساختار مطلوب در فلز جوش اتصالات فولادهای کم آلیاژ استحکام بالا (HSLA) است. در این پژوهش، فلز جوش یک فولاد HSLA جوشکاری شده توسط روش زیرپودری، در معرض فرایند اصطکاکی اغتشاشی (FSP) تحت سرعت چرخش خیلی پائین ۸۰ دور در دقیقه قرارگرفته است. بعد از FSP ساختار بینیتی درشت به ساختار فریت فوق ریزدانه تغییر کرده و اندازه دانه ها به ترتیب در قسمت بالایی و پائینی منطقه فراوری شده (منطقه اغتشاش) به حدود ۵۰۰ و ۳۰۰ نانومتر ریزدانه شد. این پژوهش یک استراتژی موثر برای ایجاد ساختار فریتی فوق ریزدانه در فلز جوش اتصالات HSLA و همچنین یک روش جوشکاری بالقوه را ارائه می کند.

 

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.

پرداخت انلاین

دیدگاه‌ها (0)

دیدگاهها

هیچ دیدگاهی برای این محصول نوشته نشده است.

فقط کاربرانی که خریدار این محصول هستند میتوانند نظر خود را ارسال کنند.