ssureHigh-pre densified solid solutions of alkaline earth

hexaborides (Ca/Sr,Ca/Ba,Sr/Ba)

and their high-temperature thermoelectric properties

محلول جامد هگزابورید قلیایی خاکی (Ca/Sr, Ca/Ba, Sr/Ba)

متراکم شده تحت فشار بالا و خواص ترموالکتریک دما بالای آن ها

ABSTRACT

Solid solutions of alkaline earth hexaborides were synthesized and densified by spark plasma sintering at 100 MPa. The high-temperature thermoelectric properties (Seebeck coefficients, electrical and thermal diffusivities, heat capacities) were measured between room temperature and 1073 K. CaB6, SrB6, BaB6 and the ternary hexaborides CaxSr1−xB6, CaxBa1−xB6, SrxBa1−xB6 (x = 0.25, 0.5, 0.75) are n-type conducting compounds over the whole compositional and thermal ranges. The values of the figure of merit ZT for CaB6 (ca. 0.3 at 1073 K) were found to be significantly increased compared to earlier investigations which is attributed to the densification process.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

محلول جامد هگزابورید های قلیایی خاکی سنتز شده و تحت زینترینگ پلاسمای جرقه ای در ۱۰۰ مگاپاسکال متراکم شد. خواص ترموالکتریک دما بالا (ضریب سیبک، نفوذ الکتریکی و حراراتی، ظرفیت گرمایی) در محدوده ی دمایی بین دمای اتاق و ۱۰۷۳ کلوین اندازه گیری شد. CaB6، SrB6، BaB6 و هگزا بورید سه تایی (CaxSr1−xB6, CaxBa1−xB6, SrxBa1−xB6 (x = 0.25, 0.5, 0.75 ترکیبات رسانای نوع N در کل محدوده های ترکیب و حرارتی هستند. مقادیر شکل بیهنه ZT برای  CaB6 به طور قابل توجهی در مقایسه با تحقیقات اخیر افزایش می یابد که وابسته به فرایند تراکم سازی است.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.

پرداخت انلاین

دیدگاه‌ها (0)

دیدگاهها

هیچ دیدگاهی برای این محصول نوشته نشده است.

فقط کاربرانی که خریدار این محصول هستند میتوانند نظر خود را ارسال کنند.