Interfacial failure mechanism in tungsten fiber reinforced copper-based composites fabricated by combustion synthesis melt infiltration under ultra-high gravity

مکانیسم گسیختگی فصل مشترکی در کامپوزیت های پایه مس تقویت شده با الیاف تنگستن تولید شده توسط رخنه دهی مذاب سنتز احتراقی تحت گرانش فوق العاده زیاد

ABSTRACT

Tungsten fiber reinforced copper-based composites were successfully fabricated by a new method called combustion synthesis melt infiltration under ultra-high gravity. Between the tungsten fibers and the copper matrix, an interlayer consisting of W18O49 needles was observed at the surface of the pickled tungsten fibers. The interfacial strength was measured by the push-out test. For the tungsten fibers with a WO 3 surface layer, the failure happened at the interface between the WO3 layer and the copper matrix by the debonding failure mechanism.For the case with the formation of a W 18O49 interlayer, the failure happened at the interface between the W18O49 interlayer and tungsten fibers by the brittle failure model, which improved the interfacial strength.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

کامپوزیت پایه مس تقویت شده با الیاف تنگستن با موفقیت به روشی جدید بنام رخنه دهی مذاب سنتز احتراقی تحت گرانش فوق العاده زیاد تولید شدند. بین الیاف تنگستن و زمینه مسی  یک میان لایه تشکیل شده از سوزن های W18O49 در سطح الیاف تنگستن اسیدشویی شده مشاهده شد. استحکام فصل مشترکی توسط تست بیرون زدگی (push-out) سنجیده شد. برای الیاف تنگستن با لایه سطحی WO3، گسیختگی در فصل مشترک بین لایه WO3 و زمینه مسی با مکانیسم گسیختگی جداشدگی (debonding failure) رخ داد. برای حالتی با تشکیل یک میان لایه W18O49، گسیختگی در فصل مشترک بین میان لایه W18O49 و الیاف تنگستن توسط حالت گسیختگی ترد رخ داد که استحکام فصل مشترکی را بهبود داد.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.