انجماد جهت‌دار آلیاژهای آلومینیوم – مس Directional solidification of aluminium–copper alloys

Directional solidification of aluminium–copper alloys

انجماد جهت‌دار آلیاژهای آلومینیوم-مس

ABSTRACT

Directional solidification experiments have been carried out on different Al–Cu alloys as a function of solidification parameters, temperature gradient G, growth rate V, and composition C0. The specimens were solidified under steady state conditions with a constant temperature gradient (7.4 K mm−1) at a wide range of growth rates (9–490 m s−1) and with a constant growth rate of 9.5 m s−1 at a wide range of temperature gradients (1.0–7.4 K mm−1). Microstructural parameters, the primary dendrite arm spacing 1, secondary dendrite arm spacing 2, dendrite tip radius R, mushy zone depth d were measured and expressed as functions of solidification parameters, G, V and C0 by using a linear regression analysis. The results were in good agreement with previous experimental work and current theoretical models suggested for dendritic growth. © 2002 Elsevier Science B.V. All rights reserved.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

در این پژوهش، انجماد جهت‌دار آلیاژهای آلومینیوم-مس با تغییر پارامترهای انجماد شامل گرادیان دمایی G، نرخ رشد V و ترکیب شیمیایی C0 انجام شد. نمونه‌ها تحت شرایط پایدار، یکبار با گرادیان دمایی ثابت K mm-1 4/7 و با نرخ رشد متغیر در محدوده -1 m sµ 490-9 و بار دیگر با نرخ رشد ثابت  -1 m sµ 5/9 و گرادیان دمایی متغیر K mm-1 4/7-1 منجمد شدند. پارامترهای ریزساختار شامل فاصله بین بازوهای دندریتی اولیه λ1، فاصله بین بازوهای دندریتی ثانویه λ2، شعاع نوک دندریت R و عمق ناحیه خمیری‌شکل d اندازه‌گیری شدند و نحوه تاثیرپذیری آن‌ها از پارامترهای انجمادی شامل G، V و C0 با استفاده از آنالیز رگرسیون خطی تعیین شد. نتایج این پژوهش، با نتایج تحقیقات پیشین و مدل‌های تئوری موجود که برای رشد دندریت‌ها پیشنهاد شده‌اند، تطبیق بسیار خوبی نشان داد.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.