خستگی خوردگی آلیاژ آلومینیوم – منیزیم بسیار ریزدانه

A microscopic study on the corrosion fatigue of ultra-fine grained

and conventional Al–Mg alloy

مطالعه میکروسکوپی خستگی خوردگی آلیاژ آلومینیوم منیزیم بسیار ریزدانه و مرسوم

ABSTRACT

The corrosion behavior of a nanocrystalline (NC)/ultrafine grained (UFG) Al–Mg based alloy was investigated and compared to its conventional counterpart 5083(H111). The corrosion fatigue (CF) was studied with respect to pit initiation, pit location and crack propagation as a function of environment. Scanning electron microscopy (SEM) with EDS was used to analyze the fracture surface of the failed specimen with respect to pitting characteristics, crack propagation and corrosion product. Load vs. cycles to failure was measured and S/N curves were generated for the UFG Al–Mg based alloy and the conventional counterpart 5083 in air and seawater.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

رفتار خوردگی آلیاژ پایه آلومینیوم منیزیزم نانوکریستالی / بسیار ریزدانه بررسی شد و با نقطه مقابل مرسوم آن 5083(H111) مقایسه شد. خستگی خوردگی با توجه به شروع حفره دار شدن، مکان حفره دار شدن و اشاعه ترک به عنوان تابعی از محیط مطالعه شد. میکروسکوپ الکترونی روبشی با آنالیز EDS برای آنالیز سطح شکست نمونه های شکسته با توجه به خواص حفره دار شدن، اشاعه ترک و محصول خوردگی انجام شد. مقدار بار برحسب سیکل شکست اندازه گیری شد و منحنی های تنش برحسب سیکل برای آلیاژ پایه آلومینیوم – منیزیم و نقطه مقابل آن آلیاژ مرسوم 5083 در هوا و آب دریا ایجاد شد.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.