خوردگی داغ مواد و مکانیزم جریان سیال

Hot corrosion of materials: a fluxing mechanism

خوردگی داغ مواد : مکانیزم جریان سیال

ABSTRACT

Hot corrosion is the accelerated oxidation of a material at elevated temperature induced by a thin  film of fused salt deposit. Fused Na2 S04 , which is the dominant salt involved in hot corrosion, is an ionic conductor, so that the corrosion mechanism is certainly electrochemical in nature.  Further, the acid/base nature of this oxyanion salt offers the possibility for the disso- lution  (fluxing) of the normally protective oxide scale. Non-protective precipitated oxide par- ticles are  often observed in the corrosion products. In this paper, the status of knowledge for the  solubilities of oxides in fused Na2 S04 is reviewed, and the effects of various influences on a  fluxing mechanism are discussed. An evaluation of a negative solubility gradient as a cri- terion  for continuing hot corrosion is made.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

خوردگی داغ مواد ، اکسیداسیون تشدید شده ای از مواد در دمای بالاست که که توسط لایه نازکی از رسوب نمک ذوب شده ایجاد می شود . Na2SO4 ذوب شده ، که در خوردگی داغ مهم ترین نمک است ، یک هادی یونی می باشد . بطوری که مکانیزم خوردگی آن کاملاً ماهیت الکتروشیمیایی دارد. علاوه بر این ، طبیعت اسیدی/بازی این نمک اکسید کننده امکان انحلال (جریان سیال) لایه اکسیدی محافظ معمولی آن را ایجاب می کند. ذرات اکسید غیر محافظ رسوب کرده اغلب در محصولات خوردگی مشاهده می شوند. در این مقاله ، وضعیت اطلاعات از حلالیت اکسید ها در نمک Na2SO4  بازنگری شده است و تاثیر عوامل تاثیرگذار بر مکانیزم جریان سیال مورد بحث قرار گرفت . یک ارزیابی ” شیب قابلیت انحلال منفی” بعنوان ملاک برای ادامه یافتن خوردگی یا انجام پذیرفته است .

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.