خوردگی SCC خط لوله از جنس API X-60 Stress corrosion cracking of API X-60 pipeline in a soil containing water خوردگی ترک ناشی از تنش در خط لوله ای از جنس API X-60 در خاکی حاوی آب ABSTRACT Stress corrosion cracking (SCC) of a API X-60 pipeline steel in a soil containing 33% water has […]
خوردگی SCC خط لوله از جنس API X-60
Stress corrosion cracking of API X-60 pipeline in a soil containing water
خوردگی ترک ناشی از تنش در خط لوله ای از جنس API X-60 در خاکی حاوی آب
ABSTRACT
Stress corrosion cracking (SCC) of a API X-60 pipeline steel in a soil containing 33% water has been investigated using slow strain rate tests and sustained load test of single-edge cracked sample. The results showed that a transgranular SCC in the soil occurred when ε˙ ≤ 3.5 × 10−7 s−1, and the susceptibility to SCC was about 30%. SCC of the cracked sample in the soil at sustained load could also occur, and the threshold stress intensity factor of SCC was KISCC =0.73KC. © 2006 Elsevier B.V. All rights reserved.
جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .
چکیده
خوردگی SCC یک فولاد خط لوله از نوع API X-60 در خاکی حاوی 33 درصد آب، با استفاده از آزمون کرنش با نرخ پایین و آزمون بار مداوم بر روی نمونه ای با ترک تک لبه مورد بررسی قرارگرفته است. نتایج نشان دادند که ترک درون دانه ای SCC در خاک، در شرایط 〖ε ̇〖≤3.5×10〗^(-7) s〗^(-1) رخ داده و در ضمن حساسیت به خوردگی SCC در حدود 30 درصد ارزیابی گردید. خوردگی SCC برای نمونه ی دارای ترک در خاک و تحت بار مداوم نیز رخ داد و فاکتور شدت تنش آستانه ای SCC K_ISCC=0.73K_C بود.