The oxidation behaviors of a ZrB2eSiCeZrC ceramic رفتار اکسایش سرامیک ZrB2-SiC-ZrC ABSTRACT The specimen of a ZrB2eSiCeZrC ceramic was heated by the electrical resistance heating and the temperature of the specimen increased linearly to 1750 C within 40s. ZrB2eSiCeZrC ceramic was oxidized in air for 30 min and the microstructure of oxide layer was investigated […]
The oxidation behaviors of a ZrB2eSiCeZrC ceramic
رفتار اکسایش سرامیک ZrB2-SiC-ZrC
ABSTRACT
The specimen of a ZrB2eSiCeZrC ceramic was heated by the electrical resistance heating and the temperature of the specimen increased linearly to 1750 C within 40s. ZrB2eSiCeZrC ceramic was oxidized in air for 30 min and the microstructure of oxide layer was investigated and discussed. The analysis of the SEM observations combined with EDS confirmed that the layered structure consisted of: (1) a SiO2-rich glass layer; (2) a thin layer of ZrO2eSiO2; (3) a layer of ZrO2 and/or ZrB2 from which SiC had been depleted; (4) unaffected ZrB2eSiCeZrC ceramic. Furthermore, the oxidation kinetics of ZrB2eSiCeZrC ceramic was investigated in detail.
جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .
چکیده
نمونه ای از سرامیک ZrB2-SiC-ZrC با گرمادهی مقاومت الکتریکی گرم شد و دمای نمونه به طور خطی تا ℃1750 در 40 ثانیه افزایش یافت. اکسایش سرامیک ZrB2-SiC-ZrC در هوا به مدت 30 دقیقه انجام شد و ریزساختار لایه اکسیدی بررسی و بحث شد. آنالیز مشاهدات SEM همراه با EDS ساختار لایه ای شامل: (1) یک لایه شیشه غنی از SiO2. (2) یک لایه نازک ZrO2-SiO2؛ (3) یک لایه ZrO2 و / یا ZrB2 از SiC تخلیه شده؛ (4) خود سرامیک ZrB2-SiC-ZrC را تایید کرد. علاوه بر این، سینتیک اکسیداسیون سرامیک ZrB2-SiC-ZrC با جزئیات بررسی شد.
جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.
نقد و بررسی‌ها
هنوز بررسی‌ای ثبت نشده است.