فرسایش کامپوزیت های کربن-کربن اصلاح شده ablation of modified carbon-carbon composites

Effect of ZrB2 and SiC distributions on the ablation of

modified carbon/carbon composites

اثر توزیع ZrB2 و SiC روی فرسایش کامپوزیت های کربن/کربن اصلاح شده

ABSTRACT

To understand the effect of introduced phases’ distribution on the ablation of carbon/carbon (C/C) composites, C/C–ZrB2–SiC composites containing isolated (SZ-1) and coupled (SZ-2) ZrB2–SiC particles were prepared via controllable precursor infiltrations and pyrolysis, respectively. Ablation under oxyacetylene torch at both Z and XY directions showed that SZ-1 had better ablation resistance than SZ-2, while the surface temperature rose up to about 2400 °C. The ablated surface morphologies showed that a relative integrate layer of ablation products was formed on SZ-1, whereas the layer on SZ-2 was defective. It was believed that the dissimilar distributions of ZrB2–SiC particles in composites resulted in distinct structures of ablation products on the surfaces and consequently their different ablation behavior.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

جهت تفهیم اثر توزیع فازهای معرفی شده روی فرسایش کامپوزیت های کربن/کربن (C/C)، کامپوزیت های C/C-ZrB2-SiC حاوی ذرات ZrB2-SiC تکی (SZ-1) و جفتی (SZ-2)، به ترتیب با روش “نفوذ تدریجی” و پیرولیز کنترل شده پیش ماده ها، آماده شدند. فرسایش تحت شعله اکسی استیلن هم در جهت Z هم در جهت XY نشان می دهد وقتی دمای سطح تا C°2400 بالا می رود، SZ-1 مقاومت به فرسایش بهتری از SZ-2 دارد. مورفولوژی سطح فرسوده شده نشان می دهد یک لایه نسبتاً کامل از محصولات فرسایش روی SZ-1 شکل گرفته است در حالیکه لایه شکل گرفته روی SZ-2 ناقص (معیوب) است. مشخص شد که توزیع نامشابه ذرات ZrB2-SiC در کامپوزیت ها، منتج به ایجاد ساختارهای مجزایی از فرآورده های فرسایش روی سطوح و در نتیجه اختلاف آنها در رفتار فرسایش می گردد.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.