مرکاپتوبنزیمیدازول بعنوان بازدارنده ی خوردگی مس در محیط کلریدی

: Mercaptobenzimidazole as a copper corrosion inhibitor

 Long-term immersion, 3D-profilometry, and electrochemistry

مرکاپتوبنزیمیدازول بعنوان بازدارنده ی خوردگی مس در محیط کلریدی:

الکتروشیمی، پروفیل سنجی سه بعدی، آنالیز سطحی XPS

ABSTRACT

The high corrosion inhibition effectiveness of 2-mercaptobenzimidazole (MBIH) in 3 wt.% aqueous NaCl solution is reported using long term immersion tests, 3D-profilometry, electrochemical impedance spectroscopy, and potentiodynamic curve measurements. The high corrosion inhibition performance was proven after 180 days of immersion. The impedance spectra were characterized by two time constants relating to charge transfer and finite layer thickness or semi-infinite diffusion of copper ions through the surface layer, therefore Cu corrosion in solution containing MBIH follows kinetic-controlled and diffusion- controlled processes. Moreover, it is shown that MBIH is a mixed-type inhibitor.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

مرکاپتوبنزیمیدازول ۲(MBOH ) بعنوان بازدارنده ی خوردگی برای مس در محلول ۳% وزنی NaCl با استفاده از اندازه گیری های EIS، منحنی پتانسیودینامیک، پروفیل سنجی سه بعدی و XPS مورد مطالعه قرار گرفت. نشان داده شده است که مس در محلولی حاوی MBOH از فرآیندهای کنترل شده با سینتیک و نفوذ پیروی می کند و MBOH یک بازدارنده ی نوع مخلوط است. ضریب نفوذ یون های مس مهاجرت کننده در لایه های سطح جامد اندازه گیری شد و بزرگی آن برابر با ۱۰-۱۵-۱۰-۴ cm2s-1 است. همچنین اثبات شده است که کمپلکس Cu(I)-MBOH روی سطح مس تشکیل شده است و ضخامت لایه ی سطحی ۱٫۴±۰٫۴nm است.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.