ABSTRACT

Melting rate (resulting from selected welding parameters) and welding speed define the heat input. As it can be changed within certain limits, melting rate and welding speed do not limit each other, but a working range is created (lower part of the figure). If the heat input is too low, i.e. too high welding speed, a definite melting of flanks cannot be ensured. Due to the poor power, lack of fusion is the result. With too high heat input, i.e. too low welding speed, the weld pool gets too large and starts to flow away in the area in front of the arc. This effect prevents a melting of the base metal. The arc is not directed into the base metal, but onto the weld pool, and flanks are not entirely molten. Thus lack of fusion may occur in such areas.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

نرخ ذوب (ناشی از پارامترهای جوشکاری انتخاب شده) و سرعت جوشکاری، گرمای ورودی را تعریف می کنند. از آنجا که می توان گرمای ورودی را در محدوده های مشخصی تغییر داد، نرخ ذوب و سرعت جوشکاری یکدیگر را محدود نمی کنند اما یک محدوه کاری ایجاد می شود (بخش پائینی شکل). اگر گرمای ورودی بسیار کم باشد یعنی سرعت جوشکاری بسیار بالا- از ذوب پهلوها نمی توان اطمینان حاصل کرد. بدلیل توان کم، عدم گدازش حاصل می شود. در صورت بیش از حد بودن گرمای ورودی یعنی سرعت جوشکاری بسیار کم، حوضچه جوش بسیار بزرگ شده و شروع به پخش شدن در ناحیه جلوی قوس می شود. این اثر، از ذوب فلز پایه جلوگیری می کند. این قوس به فلز پایه هدایت نمی شود اما روی حوضچه جوش و پهلوها بطور کامل ذوب نمی شوند. در نتیجه، عدم گدازش ممکن است در چنین نواحی ای رخ دهد.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.

s