In situ Al3Ti and Al2O3 nanoparticles reinforced Al composites produced by friction stir processing in an Al-TiO2 system کامپوزیت های آلومینیومی تقویت شده با نانوذرات درجای Al3Ti و Al2O3 تولید شده توسط فرآوری اغتشاشی اصطکاکی در یک سیستم Al-TiO2 ABSTRACT Al and TiO2 powders were selected to fabricate in situ Al composites via multiple pass […]
In situ Al3Ti and Al2O3 nanoparticles reinforced Al composites produced by friction stir processing in an Al-TiO2 system
کامپوزیت های آلومینیومی تقویت شده با نانوذرات درجای Al3Ti و Al2O3 تولید شده توسط فرآوری اغتشاشی اصطکاکی در یک سیستم Al-TiO2
ABSTRACT
Al and TiO2 powders were selected to fabricate in situ Al composites via multiple pass friction stir processing (FSP) based on the thermodynamic analysis. The microstructural investigations indicated FSP would induce reaction between Al and TiO2. Al3Ti and Al2O3 particles were formed after 4 pass FSP with 100% overlapping. The in situ particles were about 80 nm in size at various FSP conditions, and ultrafine matrix grains 602 nm in size were obtained when water cooling was applied during FSP. Tensile tests indicated that the in situ nanocomposites exhibited pronounced work hardening behavior and a good combination of strength and ductility.
جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .
چکیده
پودرهای Al و TiO2 برای تولید کامپوزیت های درجای Al از طریق فرآوری اغتشاشی اصطکاکی (FSP) چندمرحله ای مبتنی بر تحلیل ترمودینامیکی انتخاب شدند. بررسی های ریزساختاری نشان دادند که FSP باعث واکنش بین Al و TiO2 شده و ذرات Al2O3 پس از 4 مرحله FSP با 100درصد هم پوشانی تشکیل شدند. ذرات درجا، حدود nm 80 اندازه در شرایط FSP مختلف داشتند و دانه های زمینه فراریز nm 602 هنگامی که تبرید با آب در هنگام FSP اعمال شد حاصل شدند. تست های کشش نشان دادند که نانوکامپوزیت های درجا رفتار کارسختی برجسته و ترکیب خوبی از استحکام و داکتیلیته بروز دادند.