رفتار زینترینگ و مقاومت هیدروژنی دولومیت واکنشی

Sintering behaviour and hydration resistance of reactive dolomite

رفتار زینترینگ و مقاومت هیدروژنی دولومیت واکنشی

ABSTRAC

Sintering of raw dolomite and hydroxides derived from dolomite was carried out in the temperature range 1350–1650 °C. The hydroxide derived from dolomite was developed through pre-calcination of dolomite followed by its hydration. For hydroxide development, after precalcination one sample was air-quenched and the other powder was furnace cooled before hydration. The air quenched samples showed better densification than that of the furnace cooling process at the same temperature. Fe2O3 addition enhances sintering by liquid formation at higher temperature. The grain size of doloma with Fe2O3 addition is bigger than that without additive. Hydration resistance was related to densification and grain size of sintered dolomite.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

زینترینگ دولومیت خام و هیدروکسید‎های بدست آمده از دولومیت در محدوده‎ی دمایی 1350-1650 ℃انجام شد. هیدروکسید بدست آمده از زینترینگ دولومیت با تبدیلش به آهک توسط هیدراسیون بهبود پیدا کرد. برای بهبود هیدروکسید، یک نمونه پس از آهکی شدن در هوا کوئنچ شد و قبل از هیدراسیون بقیه پودر در کوره سرد شد. نمونه‎های کوئنچ شده در هوا تراکم‎پذیری بهتری از نمونه‎های سرد شده در کوره در همان دما نشان دادند. اندازه دانه دولوما با Fe2O3 اضافه شده بزرگتر از دولوما بدون افزودنی است. مقاومت هیدروژنی مربوط به تراکم‎پذیری و اندازه دانه دولومیت زینتر شده بود.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.