Oxidation mechanism of a ZrB2–SiC–ZrC ceramic heated through high frequency induction at 1600 C

سازوکار اکسیداسیون سرامیک ZrB2-SiC-ZrC حرارت داده شده از طریق القای فرکانس بالا در ℃1600

ABSTRACT

In the present work, isothermal oxidation of a ZrB2–(20 vol.%) SiC–(6 vol.%) ZrC (ZrB2–SiC–ZrC) ceramic was carried out at a constant temperature of 1600 ± 15 C in static air, and the microstructures of the surface and fractured surface of the oxidised specimen were observed using SEM. The change curve of weight change/unit area with increasing oxidation time was composed of four stages according to the increase in the oxidation time: initial, middle, middle-late and late. In the different stages, a mathematical model was formulated to interpret the oxidation behaviour of the ZrB2–SiC–ZrC ceramic at high temperature.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

در مقاله حاضر، اکسیداسیون همدمای سرامیک ZrB2-(20 vol.%) SiC-(6 vol.%) ZrC (ZrB2-SiC-ZrC) در دمای ثابت ℃15±1600 و در هوای استاتیک انجام شد و ساختار میکروسکوپی سطح و سطح شکسته نمونه اکسید شده با استفاده از SEM مشاهده شد. با توجه به افزایش زمان اکسیداسیون منحنی تغییر وزن تغییر/ سطح واحد با افزایش زمان اکسیداسیون از چهار مرحله تشکیل شده است: اولیه، میانی، میانی-پایانی و پایانی. در مراحل مختلف، یک مدل ریاضی برای تفسیر رفتار اکسیداسیون سرامیک ZrB2-SiC-ZrC در دمای بالا فرموله شد.

جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.