تحلیل کمی مقدار کاربید در فولاد 2.25Cr-1Mo-0.25V با استفاده از روش ریتولد

Quantitative carbide analysis using the Rietveld method

for 2.25Cr–1Mo–0.25V steel

تحلیل کمی مقدار کاربید در فولاد 2.25Cr-1Mo-0.25V با استفاده از روش ریتولد

ABSTRACT

It is usually difficult to quantitatively determine the mass fraction of each type of precipitates in steels using transmission electron microscopy and traditional X-ray powder diffraction analysis methods. In this paper the Rietveld full-pattern fitting algorithm was employed to calculate the relative mass fractions of the precipitates in 2.25Cr–1Mo–0.25 V steel. The results suggest that the fractions of MC, M7C3 and M23C6 carbides were evaluated precisely and relatively quickly. In addition, it was found that the fine MC phase dissolved into the matrix with prolonged tempering.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

معمولاً تعیین کمّی کسر جرمی رسوبات مختلف در فولادها از طریق میکروسکوپ الکترونی عبوری و روش های متداول پراش پرتو ایکس پودری، دشوار می باشد. در این مقاله، الگوریتم ریتولد مبنی بر برازش کامل الگوی پراش به منظور محاسبه کسر جرمی نسبی رسوبات در فولاد 2.25Cr-1Mo-0.25V استفاده شده است. نتایج نشان می دهد که می توان به سرعت و با دقت بالا، مقدار کاربیدهای MC، M7C3 و M23C6 را ارزیابی نمود. همچنین مشاهده گردید که با طولانی شدن زمان تمپر، فاز ظریف MC در داخل زمینه حل می شود.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.