ABSTRACT

The solidification process in the weld metal produces solidification structure. The solidification process depends on the thermal gradient, solidification speed and the alloy content. These structures can be planar, cellular, columnar dendritic and equiaxed dendritic. The solidification process may change from planar to cellular, columnar dendritic and equiaxed dendritic across the weld metal zone as shown in fig.1. Three grains are shown to grow epitaxially from the fusion line. A short distance away from the fusion line, solidification changes to the cellular mode. Further away from the fusion line, the solidification changes to columnar dendritic mode. Near the weld centre line equiaxed dendrites nucleate and grow, blocking off the columnar dendrites. Each one of these structures would affect the hot cracking susceptibility in greater or smaller extent.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

فرآیند انجماد در ماده‌ی جوش، ساختار انجمادی را به وجود می‎آورد. فرآیند انجماد به گرادیان دمایی، سرعت انجماد و مقدار آلیاژ بستگی دارد. ساختارها می‎توانند به صورت صفحه‎ای، سلولی، دندریتی ستونی و دندریتی هم‎محور باشند. فرآیند انجماد ممکن است از حالت صفحه‎ای به سلولی، دندریتی ستونی و دندریتی هم‎محور در سرتاسر ناحیه‎ی ماده‎ی جوش همانگونه که در شکل1 نشان داده شده است، تغییر کند.

سه دانه به منظور رشد همبافت از خط جوش نشان داده شده است. در فاصله‎ی کوتاهی دور از خط جوش، انجماد به حالت سلولی تغییر می‎یابد. دورتر از خط جوش، انجماد به حالت دندریتی ستونی تغییر می‎کند. نزدیک به خط مرکزی جوش، دندریت‎های هم‎محور جوانه زده و رشد می‎کنند، دندریت‎های ستونی مسدود می‎گردند. هر کدام از این سه ساختار روی حساسیت ترک خوردگی به مقدار بیشتر یا کمتر تاثیر می‎گذارد.