ABSTRACT
The effect of a transverse magnetic field on the growth of equiaxed grains during directional solidification of Al-10wt% Cu alloys was investigated experimentally and numerically. The experimental results show that the magnetic field has a great influence on the size and distribution of equiaxed grains. Indeed, the magnetic field causes refined and coarsen equiaxed grains to distribute on the both sides of the sample, respectively. In-situ synchrotron X-ray imaging shows that a transverse magnetic field induced some force which can act on equiaxed grains and cause the movement of equiaxed grains during directional solidification.
Numerical results reveal that the modification of the structure may be attributed to the thermoelectric (TE) magnetic effects produced by the magnetic field. Furthermore, a new method of removing inclusions in molten metal is developed by means of the TE magnetic force.
جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .
چکیده
اثر میدان مغناطیسی عرضی بر رشد دانه های هم محور حین انجماد جهت دار آلیاژ Al-10 wt% Cu به طور تجربی و عددی بررسی شده است. نتایج تجربی نشان می دهند که میدان مغناطیسی اثر بزرگی روی اندازه و توزیع دانه های هم محور دارد. در واقع، میدان مغناطیسی سبب می شود که دانه های هم محور ریز و درشت شده تا به ترتیب در هر دو طرف نمونه توزیع شوند. تصویر اشعه ایکس سنکترون درجا نشان می دهد که میدان مغناطیسی عرضی ، نیرویی مغناطیسی ایجاد می کند که می تواند روی دانه های هم محور عمل کرده و موجب حرکت دانه های هم محور حین انجماد جهت دار شود.
نتایج عددی بیان می کنند که اصلاح ساختار می تواند به اثرات مغناطیسی ترموالکتریکی (TE) تولید شده توسط میدان مغناطیسی نسبت داده شود. بنابراین، روشی جدید برای زدودن ناخالصی های فلز مذاب به وسیله نیروی مغناطیسی TE توسعه داده شد.
جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.
نقد و بررسی‌ها
هنوز بررسی‌ای ثبت نشده است.