خوردگی فرسایشی مواد برای کاشتنی های ارتوپدی

Fretting corrosion of materials for orthopaedic implants

a study of a metal/polymer contact in an

artificial physiological medium

خوردگی فرسایشی مواد برای کاشتنی های ارتوپدی :

مطالعه ارتباط فلز-پلیمر در یک محیط فیزیولوژیکی مصنوعی

ABSTRACT

The fretting corrosion behaviour of a 316L SS flat against a PMMA counterface has been investigated in an artificial physiological medium. A specific device has been used to visualize the in situ degradation at the contact interface. Simultaneous analysis of the coefficient of friction and free corrosion potential has shown four distinct stages during fretting experiments. An energy-oriented approach to the fretting process was conducted in tandem with measurement of wear. This method has shown a linear progression in the wear volume of the samples as a function of the interfacial energy dissipated during fretting. The presence of chlorides contributes to a considerable acceleration of the degradation of the stainless steel surface. This process was explained by a mechanism related to crevice corrosion activated by friction.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

رفتار خوردگی فرسایشی صفحه ای از فولاد زنگ نزن316L  با ایجاد یک لایه از جنس پلیمر PMMA در یک محیط فیزیولوژیک مصنوعی مورد ارزیابی قرار گرفت. دستگاه خاصی به کار برده شد تا در شرایط طبیعی، تخریب در محل تماس فصل مشترک فرض شود. تحلیل همزمان ضریب اصطکاک و پتانسیل خوردگی مستقل، چهار مرحله مجزا در طی آزمایشات فرسایشی را نشان داد. پیش رفت انرژی پخش شده در حین فرایند فرسایش، با اندازه گیری سایش در تاندم انجام شد. این روش پیشرفت طولی در مقدار سایش نمونه ها را به عنوان یک تابع از انرژی پراکنده شده در فصل مشترک در طی فرسایش نشان می دهد. حضور کلراید ها با سرعت قابل توجه به تخریب سطح فولاد زنگ نزن کمک می کند. این فرایند به وسیله ی یک مکانیزم وابسته به خوردگی شکافی که با اصطکاک فعال شده، بیان می شود.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.