زینترینگ سرامیک های Nd:YAG شفاف تحت اتمسفر اکسیژن

Sintering of transparent Nd:YAG ceramics in oxygen atmosphere

زینترینگ سرامیک های Nd:YAG شفاف تحت اتمسفر اکسیژن

ABSTRACT

Yttrium aluminum garnet (YAG) transparent ceramics were fabricated by sintering at oxygen atmosphere. Tetraethyl orthosilicate (TEOS) was added as the sintering additive to control the grain growth and densification. Pores were eliminated clearly at temperature lower than 1700 °C, while grain size was around 3 μm. The in-line transmittance was 80% at 1064 nm when samples were sintered at 1710 °C. The effect of TEOS was studied in oxygen atmosphere sintering for Nd:YAG transparent ceramics. At higher temperature like 1710 °C, the grain growth mechanism was solute drag, while at 1630 and 1550 °C the grain growth was controlled by liquid phase sintering mechanism. And 0.5 wt.% TEOS was the best adding content for Nd:YAG sintered in oxygen atmosphere.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

سرامیک‎های ایتریم آلومینوم گارنت (YAG) شفاف توسط زینترینگ تحت اتمسفر اکسیژن تهیه شدند. به منظور کنترل رشد دانه و تراکم سازی تترا اتیل اورتو سیلیکات (TEOS) به عنوان افزودنی زینترینگ اضافه شد. حفرات به طور واضح در دمای کمتر از C˚1710 حذف شدند، در حالی که اندازه‎ی دانه تقریباً μm3 بود. زمانی‎که نمونه‎ها تحت دمای C˚1710 زینتر شدند، عبور خطی 80% در طول موج nm1064 حاصل گردید. تاثیر TEOS در زینترینگ تحت اتمسفر اکسیژن سرامیک‎های شفاف Nd:YAG مورد مطالعه قرار گرفت. در دماهای بالاتر از C˚1710، مکانیزم رشد دانه توسط کشش جزء حل شده یا انتقال حجمی صورت می‎پذیرد، در حالی که در دماهای C˚1550 و 1630 رشد دانه از طریق مکانیزم زینترینگ فاز مذاب انجام می‎شود، و مقدار بهینه TEOS برای زینترینگ سرامیک های Nd:YAG تحت اتمسفر اکسیژن 5/0% وزنی بدست آمد.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.