نانوپودرهای آلومینیوم و تعیین مقدار آلومینیوم فلزی در آن

Quantitative X-ray Rietveld analysis of metallic aluminum content in nano-aluminum powders

تحلیل کمّی مقدار آلومینیوم فلزی با آنالیز پرتو ایکس ریتولد در نانوپودرهای آلومینیوم

ABSTRACT

Accurate analysis of the content of metal aluminum (Al) in nano-Al powders is a difficult task due to the high reactivity of nano-Al powders. Here, the X-ray Rietveld quantitative phase analysis (QPA) method was applied to analyze the content of metal aluminum in nano-Al powders produced by three methods. A good agreement between the observed and calculated diffraction pattern was obtained and the conventional Rietveld factors ( R p, Rwp and GOF) converged to satisfactory values, which suggested that Al content was evaluated accurately. At the same time, the mixture sample of 89.77 wt.% micro-Al+10.23 wt.% α- Al 2O3 was study and the fitting pattern and R factors were satisfactory, which further verified the reliability of the X-ray Rietveld QPA method.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

به دلیل فعالیت بالای نانوپودر آلومینیوم، شناسایی دقیق میزان آلومینیوم فلزی (Al) در نانوپودرهای آلومینیوم بسیار دشوار است. در این پژوهش، روش تحلیل کمّی فاز (QPA) ریتولد مبتنی بر پرتو ایکس مورد استفاده قرار گرفت تا در نانوپودرهای آلومینیوم تهیه شده به سه روش متفاوت، مقدار دقیق آلومینیوم فلزی موجود تعیین شود. تطابق خوبی میان الگوهای پراش مشاهده و محاسبه شده به دست آمد و ضرایب معمول ریتولد (Rp، Rwp و GOF) به مقادیر مطلوبی همگرا شدند که این امر نشان می دهد که مقدار آلومینیوم به درستی ارزیابی شده است. همچنین مخلوط 89.77 درصد وزنی micro-Al و 10.23 درصد وزنی Al2O3 مورد بررسی قرار گرفته و الگوهای برازش و ضرایب R به درستی به دست آمدند که این نیز تأییدکننده درستی و قابلیت اطمینان روش ریتولد می باشد.

 جهت دانلود ترجمه تخصصی و فارسی این مقاله می توانید وجه آنرا پرداخت نموده و بلافاصله دریافت نمایید.